SCM445 /50CrMo4/din 1.7228/4145 hot forged steel price per kg, forged steel bar, Small MOQ
AISI 4145H MOD Steel is a chromium molybdenum alloy steel grade widely used in the oil and gas sectors. Similar to AISI 4140 but with a higher carbon content. AISI 4145H MOD Steel is more popular in larger diameters due to its increased strength and harden-ability. AISI 4145H MOD Steel is commonly supplied quenched and tempered with a hardness of between 30 to 36HRc. AISI 4145H MOD Steel is commonly used for a variety of applications in the oil and gas sector. Used often for the manufacture of down hole drilling tools such as drill collars. Other applications include gears, shafts for hydraulic presses, rolls for paper mills, pump shafts and tool holders.
ASTM A29 Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General
API 7 Specification for Rotary Drill Stem Elements.
Chemical Composition (%)
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Cu(％) |
|---|---|---|---|---|---|---|---|
| 0.42～0.49 | 0.65 ~ 1.10 | 0.75 ~ 1.20 | ≤0.035 | ≤0.040 | 0.15～0.25 | 0.15 ~ 0.30 | ≤0.25 |
Grain Size: The austenitic grain size shall be 6-9 as defined in ASTM E-112.
Process: EAF+LF+VOD+Forged+Heat Treatment(optional)
Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of eachAISI 4145H MOD Steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of AISI 4145H MOD Steel.
Annealing: Heat the steel slowly to 800-850°C and allow enough time for the steel to be thoroughly heated. Cool slowly in the furnace to 480°C followed by air cooling.
Stress Relieving: When parts are heavily machined, ground or otherwise subject to cold work, stress relieving will be beneficial prior to hardening.
Hardening: AISI 4145H MOD Steel is usually supplied ready heat treated to 30-36HRc. If further heat treatment is required annealed AISI 4145H MOD Steel should be heated slowly to 840-875°C and after adequate soaking at this temperature quench in oil. Temper as soon as the tools reach room temperature.
Tempering: Heat carefully to a suitable temperature selected by reference to a tempering chart or table (usually between 550-700°C, soak at the temperature for 2 hours per 25mm of ruling section, then allow to cool in air. Tempering between 250-375°C is not advised as tempering within this range will seriously reduce the impact values of this steel.
SIZE RANGE:
Round:
Hot Forged: 80mm -1200mm
SURFACE FINISHES:
Black, Peeled (K12), Turned & Polished (H10, H11),
Test: Ultrasonic test according to SEP 1921-84