SHANGHAI UNITE STEEL
One-stop Brand Service Provider For Globle Machinery And Petrochemical Enterprise And Special Steel Distributor.
Add to Cart
Features:
1. Competitive price
2. Immediate delivery
3. Premium quality
4. Reliable service
5. MOQ: 1 Ton
| Packing details | In seaworthy packing, as your requirement. |
| Delivery details | within 30-50 days |
Chemical Composition:
| Grade | C | Si | Mn | P | S | Cr | Mo | V |
| 1.2365 |
0.35- 0.45 |
0.80- 1.25 |
0.20- 0.70 |
0.030 max | 0.030 max |
3.00- 3.75 |
2.00- 3.00 |
0.25- 0.75 |
DIN 1.2365 H10 Hot Work Tool Steel
Similar Grade: DIN 1.2365, H10
Shape: Round, Flat, Square.
Size Range:
| Diameter(mm) | Thickness (mm) | Width (mm) | Length(mm) | |
| Round | 50-420 | - | - | 2000-5800 |
| Square | 50-420 | - | - | 2000-5800 |
| flat | - | 20-200 | 80-600 | 2000-5800 |
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Heat Treatment:
FORGING: Heating for forging must be done slowly and uniformly. Soak through at 1900-2000°F, and reheat as often as necessary, stopping work when the temperature drops below 1650°F. After forging cool slowly in lime, mica, dry ashes or furnace. H10 hot work tool steel should always be annealed after forging.
ANNEALING: Heat slowly to 1550-1650°F, hold until the entire mass is heated through, and cool slowly in the furnace (40°F per hour) to about 1000°F, after which the cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
SRAIN RELIEVING: stress reliving when desirable to relieve the strains of machining, heat slowly to 1050-1250°F, allow to equalize, and then cool in still air.
HARDENING: Warm slightly before charging into the preheat furnace, which should be operating at about 1400-1500°F. 1.2365 hot work tool steel is a very deep hardening steel, and although oil quenching may be used where maximum hardness is required, air hardening is recommended for most applications. The use of salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening spent pitch temperature employed Annealing is usually in the range of 1800-1900°F.
TEMPERING: Tempering practice may vary with size and application, but is usually performed in the temperature range of maximum secondary hardness or higher double tempering is recommended.
Forging dies for steel, mandrels, dies, die holder bolsters and dummy blocks, punches, die inserts, gripper and header dies, hot shears, aluminum die casting dies.
Product Description:
1.2365 Chromium hot work tool steel has excellent resistance to softening at high temperatures. This particular grade is resisitant to thermal fatigue cracking and can be cooled in water for servicing.