ASTM A182 F22 Hot-forged-steel-bar, forged steel bar, Small MOQ
Application
A182 F22 steel is a low alloy steel containing nominally 2.25% Chromium. This A182 F22 steel is widely used in the oil patch wellhead applications for connectors, hangers and block valves. Hardness levels up to 22 HRC are approved to NACE MR0175. The grade is often used as the base metal for clad components. If supplied to ASTM A182 in the normalised and tempered condition, the 0.2% Proof Stress minimum is 30 KSI.
Material no. DIN ASTM
1.7380 10CrMo9-10 A182 F22
2”∅ – 36”∅
Chemical Composition(%)
| C | Mn | Si | P | S | Cr | Mo |
|---|---|---|---|---|---|---|
| 0.05-0.15 | 0.30-0.60 | 0.50 max | 0.040 max | 0.040 max | 2.00-2.50 | 0.87-1.13 |
| Delivery Condition | Tensile Strength Rm (Mpa) | Yield Strength Rp0.2 (Mpa) | Elongation(%) | Reduction Ratio(%) | Hardness (HB) |
|---|---|---|---|---|---|
| Normalized and Tempered | 900 min | 675 min | / | / | / |
| Slow Cooling | 415 min | 205 min | 20 min | 35 min | 170 max |
Normalizing: Temperature: 920°-980°C.
Stress Relieving: Stree relieving to remove maching stresses should be carried out by heating to 675°C, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Austenization: Temperature:920°-980°C
Tempering: Tempering temperature: 650°-750°C
Forging: Hot forming temperature: 850°-1050°C